Analisis Pengaruh Variasi Arus dan Sudut Kampuh terhadap Struktur Mikro, Kekerasan, dan Ketangguhan Impact pada Material SS410 dengan Menggunakan Metode Las SMAW

Andi Idhil Ismail, Ahmad Fitrianto

Abstract


This study aims to assess the effect of variations of welding current and bead angle of 60o and 80o on the the mechanical properties and the appropriate welding method as a connector for two SS 410 using the SMAW welding method (Shielded Metal Arc Welding). The current variations are 85 A, 90 A, 110 A and groove type with V-angle of 60o and 80o. After the spesimen welding process, the microstructure, vickers, and impact strenght were tested. The results obtained showed that the highest hardness value occured in 110 A currents with 80o angle of motion at 165 VHN in the HAZ region (1) which has ferrite and carbide structure that makes the area hard. The highest value of impact toughness (K) at 60o angle is occured at 85 A current with a value of 1,294 Joule / mm2. The highest value of impact toughness (K) at 80o angel occured at 85 Ampere current with a value of 1,831 Joule / mm2. Using angle of 80o with each current of 110 A and 85 A the optimum hardness and impact properties can be obtained

Keywords :SS 410 Material, Impact, Hardness, SMAW

Abstrak

Penelitian ini bertujuan untuk mengetahui pengaruh variasi arus 85 Ampere (A), 90 Ampere (A), 110 Ampere (A) dan sudut kampuh V sebesar 60o dan 80o terhadap pengujian sifat mekanik serta metode pengelasan yang tepat guna sebagai penyambung dua material SS 410 dengan menggunakan metode las SMAW (Shielded Metal Arc Welding). Variasi arus menggunakan arus sebesar 85 A, 90 A, 110 A dan sudut kampuh V sebesar 60o dan 80o. Setelah proses pengelasan spesimen selanjutnya dilakukan pengujian struktur mikro, kekerasan (vickers), dan ketanguhan impact. Hasil penelitian yang didapat menunjukkan nilai kekerasan tertinggi terjadi pada arus 110 A dengan sudut kampuh 80o sebesar 165 VHN pada daerah HAZ (1) yang memiliki struktur ferrit dan karbida yang membuat daerah tersebut menjadi keras. Nilai tertinggi ketangguhan impact (K) pada sudut kampuh 60o terjadi pada kuat arus 85 A dengan nilai sebesar 1,294 Joule/mm2. Nilai tertinggi ketangguhan impact (K) pada sudut kampuh 80o terjadi pada kuat arus 85 A dengan nilai sebesar 1,831 Joule/mm2. Untuk mendapatkan nilai kekerasan dan hasil ketangguhan impact yang baik yaitu menggunakan sudut kampuh 80o dengan masing - masing arus sebesar 110 A dan 85 A.

 Kata kunci :Baja SS 410, Impact, Kekerasan, SMAW


 


References


Ferry M.P, Tumpal O.R, Yusup Hendronursito, "Analisa Variasi Arus Menggunakan Las GTAW Pada Material SS JIS 410J1 Dengan Filler ER308L," Jurnal Rekayasa, Teknologi dan Sains., vol. 2, no. 1, pp. 40-42, 2018.

Joko Santoso, "Pengaruh Arus Pengelasan Terhadap Kekuatan Tarik Dan Ketangguhan Las SMAW Dengan Elektroda E7018, "Semarang: Universitas Negeri Semarang. Tersedia:https://lib.unnes.ac.id/755/1/1902.pdf diunduh 17 Mei 2019.

Subardi, "Pengaruh dari suhu area pemanasan terhadap kekerasan dan mikrostruktur pada pengelasan baja ST 37," 2009.

Fajar Nugroho, "Studi Komparasi Pengaruh Variasi Arus Pengelasan Terhadap Kekuatan Impak, Kekerasan Dan Stuktur Mikro Sambungan Las Pegas Daun Baja SUP 9 Pada Proses Las SMAW," Jurnal Ilmiah Bidang Teknologi., vol. 9, no. 2, pp. 61-62, 2017.

Sonawan, H., Suratman, R, Pengantar Untuk Memahami Pengelasan Logam. Bandung: Alfa Beta, 2004.

Miftahul Huda, Ferry Setiawan, "Pengaruh Variasi Sudut Kampuh V Dan Kuat Arus Dengan Las Shielded Metal Arc Welding (SMAW) Pada Baja A36 Terhadap Sifat Mekanik," Jurnal Ilmiah Teknik Mesin Umsida., pp. 5-6, 2016.

Samuel, Akhmad R.A, Sarjito Jokosisworo, "Pengaruh Kuat Arus Listrik, Temperatur Dan Variasi Sudut Kampuh Terhadap Kekuatan Impact Alumunium 5083 Pengelasan GTAW Dengan Gas Pelindung Helium," Jurnal Teknik Perkapalan., vol. 4, no. 1, pp. 301-303, 2016.

Hammada Abbas, Ahmad Yusran Aminy, Munawar, "The Effects of Shielded Metal Arc Welding (Smaw) Welding On The Mechanical Characteristics With Heating Treatment inn S45c Steel," J. Phys., vol , 2018

B Ravindra M, C.L.Dhamejani, "Influence of Welding Speed and Groove Angle on Strength of V-Groove Butt Weld Joint Using TIG Welding, "International Journal of Engineering Sciences & Research Technology., pp. 339-340, 2016.




DOI: https://doi.org/10.32487/jst.v5i2.687

Refbacks

  • There are currently no refbacks.


View My Stats