Sintesis Komposit N-TIO2/Bentonit dan Karakterisasi Menggunakan FTIR

Emas Agus Prastyo Wibowo

Abstract


Abstract

Titanium Dioxide (TiO2) is a semiconductor material that is relatively inert compared with other compounds, and also serves as a photocatalyst which has fotoaktifitas and high stability. The presence of dopant N on TiO2 matrix will reduce the band gap of  TiO2 so that shift the absorption spectrum from UV to visible light that are abundant in sunlight. Besides the addition of dopants on TiO2 matrix, the addition of bentonite can also increase the photocatalytic activity of TiO2. The main absorption peak-uptake at N-TiO2/ bentonite is still the same with bentonite which is in wavenumber 3626.17 cm-1, 3448.72 cm-1  and 1635.64 cm- Based on the interpretation of the spectra of FT-IR composite of Bentonite, TiO2 /bentonite, and N-TiO2/ bentonite produced can be concluded that no significant changes between the functional groups and bentonite as composite TiO2-bentonite and N-TiO2 / Bentonite

 

Keywords: FTIR, composite, titanium dioxide

 

Abstrak

Titanium Dioksida (TiO2) merupakan bahan semikonduktor yang relatif inert dibandingkan dengan senyawa-senyawa lain dan juga berfungsi sebagai fotokatalis yang memiliki fotoaktifitas dan stabilitas tinggi. Adanya dopan N dalam matriks TiO2 akan  memperkecil band gap TiO2 sehingga terjadi pergeseran penyerapan spektrum sinar dari sinar UV ke sinar tampak yang tersedia melimpah dalam sinar matahari. Selain dengan penambahan dopan pada matriks TiO2, penambahan bentonit juga dapat meningkatkan aktifitas  fotokatalitik dari TiO2. Puncak serapan-serapan utama pada N-TiO2/bentonit masih sama dengan bentonit yang berada di bilangan gelombang 3626.17 cm-1, 3448.72 cm-1 dan 1635.64 cm-1. Berdasarkan interpretasi spektra FT-IR komposit dari Bentonit, TiO2/bentonit, dan N-TiO2/bentonit yang dihasilkan dapat disimpulkan bahwa tidak terjadi perubahan gugus fungsi yang signifikan antara bentonit sebagai dan komposit TiO2-Bentonit dan N-TiO2/Bentonit.

 

Kata kunci: FTIR, komposit, titanium dioksida


Keywords


FTIR, composite, titanium dioxide

Full Text:

PDF

References


Hoffman, M.R., Martin, S.T., Choi, W.,and Bahnemann, D.W. (1995). Environemntal Applications Of Semiconductor Photocatalysis. Chemical Review, 95 (1), 69-96.

Yin, W.J., Chen, S., Yang, J.H., Gong, X.G., Yan, Y., Wei, S.H. (2010).Effective Band Gap narrowing of Anatase TiO2 by Strain Along a Soft Crystal Direction, Applied Physics Letter, 96.

Viswanathan, B., Krishanmurthy, K.R..(2012). Nitrogen Incorporation in TiO2 : Does It Make a Visible Light Photo-Actve Material, International Journal of Photoenergy, 1-10.

Darzi, S.J., Mahjoub, A.R., Sarfi, S., 2012. Visible-Light-Active Nitrogen Dopen TiO2 Nanoparticle Prepared by Sol-Gel Acid Catalyzed Reaction. Iranian Journal of Materials Science & Engineering, 9 (3),17-23.

Wawrzyniak, B., Janus, M., Grzmil, B., dan Morawski, A.W., 2007. TiO2 Preparation Of The TiO2 Photocatalyst Using Pressurized Ammonia, Polis Journal Of Chemical Technology, 9 (1): 51-56.

Supeno, M., 2007. Bentonit Alam Terpilar Sebagai Material Katalis/Co-Katalis Pembuatan Gas Hidrogen Dan Oksidasi Dari Air. Tesis. Universitas Sumatera Utara. Medan.

Ramadhana, A. K. K., Wardhani, S., Purwonugroho, D (2013). Fotodegradasi zat warna methyl orange menggunakan TiO2-zeolit dengan penambahan ion persulfat, skripsi, FMIPA, Universitas Brawijaya.

Ariyanti, D. S, 2012, Pengaruh Penambahan Oksidator H2O2 terhadap Degradasi Zat Warna Methyl Orange dengan Fotokatalis ZnO-Zeolit, Skripsi, Fakultas Matematika dan Ilmu pengetahuan Alam, Universitas Brawijaya.

Fatimah, I., Sugiharto, E., Wijaya, K., Tahir, I., dan Kamleia. (2006). Titanium Oxide Dispersed On Natural Zeolite (TiO2/Zeolit) And Its Application For Congo Red Photodegradation. Indo J. Chem, 6 (1): 38-42.

Saraswati A, Nugraha I. 2014. Sintesis Komposit Montmorillonit-TiO2 dan Aplikasinya untuk Pengolahan Limbah Cair Pabrik Gula. Prosiding Seminar Nasional Kima dan Pendidikan KimiaVI. 501-511.

Aji, N. R., Wibowo, E. A. P., Ujiningtyas, R., Wirasti, H., & Widiarti, N. (2016). Sintesis Komposit TiO2-Bentonit dan Aplikasinya untuk Penurunan BOD dan COD Air Embung UNNES. Jurnal Kimia VALENSI, 2(2), 114-119.

Zhang, H., Yang, Z., Zhang, X., Maio, N., (2014). Photocatalytic Effect of Wool Fibers

Modified with Soley TiO2 Nanoparticles and N-doped TiO2 Nanoparticles by Using Hydrothermal, Elsivier, 254, 106-114

Febriana, I. D. (2011). Pengaruh pH Awal Larutan Methyl Orange pada Degradasi Zat Warna Methyl Orange dengan Fotokatalis Bentonit-TiO2, Jurnal, FMIPA, Universitas Brawijaya.

Putri, O.A., Wardhani, S., Tjahjanto, R.T. (2015). Degradasi Methyl Orange dengan TiO2-N/Bentonit Kajian: Komposisi N Pada Komposit TiO2-N/Bentonit, Sumber Sinar, dan Volume H2O2. Kimia Student Journal, 1(1), 670-676.

Wibowo, E.A.P., Aji, N.R., Ujiningtyas, R., Mayasari, T., Widiarti, N. (2016). Fotokatalis TiO2/Kitosan dan TiO2/Bentonit sebagai Penjernih Air Embung di Lingkungan Unnes. Jurnal Sains dan Teknologi, 5(2), 807-812.




DOI: https://doi.org/10.32487/jtt.v5i1.218

Refbacks

  • There are currently no refbacks.


JTT (Jurnal Teknologi Terpadu) has been indexed by:

 

 

 

 

 

 

 

 

 

Web Analytics

JTT Visitor Stats