Pembuatan Hydroxyapatite Dari Limbah Cangkang Telur Bebek Menggunakan Metode Sol Gel Dengan Pelarut Asam Nitrat
Abstract
This study aims to determine the effect of nitric acid concentration and stirring speed on the Ca/P molar ratio through the formation of Precipitated Calcium Carbonate (PCC) from duck eggshells and to analyze the size and shape of hydroxyapatite crystals. Duck eggshell waste from Jl. Mojosari, Sumbersuko District, Lumajang Regency, was used as the raw material. The research process consisted of three stages: (1) Calcination of eggshells, (2) Synthesis of PCC by dissolving duck eggshells in 2 M HNO₃, and (3) Synthesis of hydroxyapatite by mixing PCC with (NH₄)₂HPO₄ at pH 9. The results showed that (1) Nitric acid concentration affects the Ca/P molar ratio, where a higher nitric acid concentration leads to a lower Ca/P molar ratio, with a Ca/P molar ratio of 4.1599 at a concentration of 0.6 M and a stirring speed of 500 rpm, (2) Stirring speed also affects the Ca/P molar ratio, where a higher stirring speed results in a lower Ca/P molar ratio, and (3) The hydroxyapatite crystal size under these conditions was 116.3322 nm, with a rough crystal surface.
Keywords
Full Text:
PDFReferences
(1) Adinda, A. (2020) ‘Karakterisasi Morfologi dan Rasio Ca/P Hidroksiapatit Tulang Ikan Cakalang (Katsuwonus Pelamis)’, Jurnal Kedokteran, 5(6), pp. 34-36
(2) Afifah, F. and Cahyaningrum, S.E. (2020) ‘Sintesis dan Karakterisasi Hidroksiapatit dari Tulang Sapi (Bos Taurus) menggunakan Teknik Kalsinasi’, UNESA Journal of Chemistry, 9(3), pp. 190–191
(3) Agustiyanti, R.D. et al. (2018) ‘Sintesis Hidroksiapatit dari Precipitated Calcium Carbonate (PCC) Cangkang Telur Ayam Ras Melalui Proses Presipitasi’, Jurnal Online Mahasiswa Fakultas Teknik, 5(1), pp. 1–2
(4) Akbar, A.F. et al. (2021) ‘Sintesis dan Karakterisasi Hidroksiapatit Tulang Ikan Baung (Hemibagrus Nemurus Sp.) debagai Kandidat Implan Tulang’, Jurnal Kimia Riset, 6(2), pp. 94–95
(5) Andyana, N.S., Amalia, A.R. and Sumada, K. (2021) ‘Kajian Hydroxyapatite dari Cangkang Kupang Putih dan Asam Fosfat’, Journal of Chemical and Process Engineering, 2(3), pp.1–2
(6) Audrya, H., Azis, Y. and Akbar, F. (2018) ‘Sintesis Hidroksiapatit dari Precipitated Calcium Carbonate (PCC) Cangkang Telur Ayam Ras Melalui Proses Sol Gel dengan Variasi Waktu Reaksi dan Waktu Aging’, Jurnal Online Mahasiswa Fakultas Teknik, 5(1), pp. 3–4
(7) Fitriani, E., Isdadiyanto, S. and Tana, S. (2016) ‘Kualitas Kerabang Telur pada Berbagai Itik Petelur Lokal di Balai Pembibitan dan Budidaya Ternak Non Ruminansia (BPBTNR), Ambarawa’, Jurnal Berkala Ilmiah Biologi, 18(2), pp. 2–3
(8) Hakim, L., Dirgantara, M. and Nawir, M. (2019) ‘Karakterisasi Struktur Material Pasir Bongkahan Galian Golongan C Dengan Menggunakan X-Ray Difraction (X-RD) Di Kota Palangkaraya’, Jurnal Jejaring Matematika dan Sains, 1(1), pp. 44–45
(9) Hanifah, H.N. (2023) ‘Perbandingan Efektivitas Cangkang Telur Ayam dan Cangkang Telur Bebek sebagai Bioadsorben Logam Zn Dengan Metode Spektrofotometri Serapan Atom (SSA)’, Jurnal Sabdariffarma, 10(2), pp. 2–3
(10) Hariyati, Shofiyani, A. and Agus Wibowo, M. (2019) ‘Ekstraksi Kalsium Karbonat (CaCO3) dari Bahan Dasar Cangkang Kerang Ale-Ale (Meretrix Meretrix) Pada Temperatur Kalsinasi 500°C’, 8(1), pp. 56–57
(11) Haruda, Fadli and Yenti. (2016) ‘Pengaruh pH dan Waktu Reaksi pada Sintesis Hidroksiapatit dari Tulang Sapi dengan Metode Presipitasi’, Jurnal Teknik, 3(1), pp. 1-7
(12) Henggu, K.U., Ibrahim, B. and Suptijah, P. (2019) ‘Hidroksiapatit Dari Cangkang Sotong Sebagai Sediaan Biomaterial Perancah Tulang’, Jurnal JHPI, 22(1), pp. 2–3
(13) Kartikasari, D. (2021) ‘Potensi Cangkang Telur Bebek dan Telur Puyuh Sebagai Antasida dengan Metode Kapasitas Penetralan Asam’, Jurnal Ilmiah Pharmacy, 8(2), pp. 2–3
(14) Mahdi, Z. et al. (2020) ‘Sintesis Hidroksiapatit dari Precipitated Calcium Carbonate (PCC) Terumbu Karang Melalui Proses Presipitasi dengan Variasi Rasio Ca/P Dan Ph’, Jurnal Online Mahasiswa Fakultas Teknik, 7(2), pp. 2–3
(15) Maisyarah, A.O. and Shofiyani, A. (2019) ‘Sintesis CaO dari Cangkang Kerang Ale-Ale (Meretrix Meretrix) pada Suhu Kalsinasi 900 °C’, 8(1), pp. 32–33
(16) Malau, N.D. (2020) ‘Penentuan Suhu Kalsinasi Optimum CaO dari Cangkang Telur Bebek dan Cangkang Telur Burung Puyuh’, Jurnal EduMatSains, 4(2), p. 194
(17) Ngapa, Y.D. (2018) ‘Sintesis Dan Karakterisasi Hidroksiapatit (HAp) Dari Limbah Cangkang Kerang Lokan (Batissa Violacea L) Dengan Metode Basah Presipitasi’, Jurnal Dinamika Sains, 2(1), p. 67
(18) Ningsih, S.K.W. (2016), Sintesis Anorganik, Padang, UNP Press
(19) Prasetyawan, E.D. (2023) ‘Pengaruh Waktu Kalsinasi Pada Sintesis Hidroksiapatit Berbasis Cangkang Telur Ayam Untuk Aplikasi Biomaterial’, Jurnal Teknik Mesin, 11(2), p. 19
(20) Puspita, F.W. (2017) ‘Sintesis Dan Karakterisasi Hidroksiapatit Dari Cangkang Telur Ayam Ras (Gallus Gallus) Menggunakan Metode Pengendapan Basah’, UNESA Journal of Chemistry, 6(2), p. 101
(21) Putri V, D., (2016) ‘Pengaruh Perbandingan Molar Ca/P dalam Pembuatan Lapisan Tipis Kalsium Fosfat dari Prekursor Ca(NO3)2.4H2O melalui Metode Sol-Gel’, Jurnal Katalisator, 25(2), pp 3-5
(22) Qalbi, T., Azis, Y., dan Helwani, Z. (2018) ‘Sintesis Hidroksiapatit Melalui Precipitated Calcium Carbonate (PCC) Cangkang Telur Ayam Ras dengan Metode Presipitasi pada Variasi Konsentrasi Pelarut HNO3 dan Rasio Ca/P’, Jurnal FT Teknik, 5(1), pp 4-5
(23) Rahmawati, Suwito, Mangiwa S. (2020) ‘Sintesis dan Karakterisasi Hidroksiapatit dari Cangkang Telur Ayam’, AVOGADRO Jurnal Kimia, 4(2), p. 111
(24) Setiawan, A. et al. (2023) ‘Sintesis Biomaterial Hydroxyapatite dengan Proses Flame Spray Pyrolysis Disertai Penambahan Aditif Organik ‘, Jurnal Teknik Kimia, 16(4), p. 190
(25) Setiyawan, A.I., Karimy, M.F., dan Erwinda Z. (2021) ‘Karakteristik Mikro Struktur Dan Komposisi Cangkang Telur Unggas Domestikasi Dengan Menggunakan Sem Dan Xrf’, Jurnal Prosiding Seminar Teknologi dan Agribisnis Peternakan, 5(2), p. 492
(26) Sinulingga, K. dan Sirait, M. (2021), Hidroksiapatit dari Batu Kapur dan Aplikasi, Medan, Yayasan Kita Menulis
(27) Wahyudi, P., Alimuddin, A.H., Shofiyani, A. (2020) ‘PengaruhWaktu Aging terhadap Sifat Hidrofobisitas Silika Xerogel Termodifikasi Trimetilklorosilan’, Journal of Pure and Applied Chemistry, 3(1), p. 19
(28) Warastuti, Y., Abbas, B., Suryani, N. (2017) ‘Konversi Koral Laut Menjadi Hidroksiapatit dengan Metode SonikasI’, Jurnal Kimia dan Kemasan, 39(2), pp. 80-81
(29) Wardiana, A. (2019) ‘Pemanfaatan Batu Kapur Sebagai Bahan Baku Hidroksiapatit’, Journal of Chemistry, 8(2), pp. 133-135
DOI: https://doi.org/10.32487/jtt.v14i1.2459
Refbacks
- There are currently no refbacks.
JTT (Jurnal Teknologi Terpadu) has been indexed by:
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|